68
V. P. Drachev et al.
Fig. 3.13 a Experimental absorbance of Co-NPs in hexane. As grown Co-NPs (red), after 1 h
sonication with external 130 mT DC magnetic field (blue), after 2.5 h sonication with external 130
mT DC magnetic field (green, plasmon peak is demolished), magnetic field is off and 1 h sonication
(black). b Co-NPs size distribution measured with dynamic light scattering (red)-as grown; (green)
-2.5 h sonication with external 130 mT DC magnetic field; (black) after 1 h sonication without
magnetic field. From [2] with permission licensed under CC BY 4.0 https://creativecommons.org
Fig. 3.14 Dynamic light scattering (DLS) size distribution of Co nanoparticles (a), as grown
sample; (b), after 2.5 h sonication with external 130 mT DC magnetic field; and (c), after 1 h
sonication without external magnetic field. From [2] with permission licensed under CC BY 4.0
https://creativecommons.org
V. P. Drachev et al.
Fig. 3.13 a Experimental absorbance of Co-NPs in hexane. As grown Co-NPs (red), after 1 h
sonication with external 130 mT DC magnetic field (blue), after 2.5 h sonication with external 130
mT DC magnetic field (green, plasmon peak is demolished), magnetic field is off and 1 h sonication
(black). b Co-NPs size distribution measured with dynamic light scattering (red)-as grown; (green)
-2.5 h sonication with external 130 mT DC magnetic field; (black) after 1 h sonication without
magnetic field. From [2] with permission licensed under CC BY 4.0 https://creativecommons.org
Fig. 3.14 Dynamic light scattering (DLS) size distribution of Co nanoparticles (a), as grown
sample; (b), after 2.5 h sonication with external 130 mT DC magnetic field; and (c), after 1 h
sonication without external magnetic field. From [2] with permission licensed under CC BY 4.0
https://creativecommons.org