454
I. I. Gab et al.
Fig. 6 Dependence of the zirconia ceramics surface area covered with a double chromium-silver
film on the annealing time at different temperatures (900–1100 ºS)
Fig. 7 The joint of zirconia ceramics, through a double film of Cr–Ag, with ultrathin welding seam
which was made by pressure welding, ×600
I. I. Gab et al.
Fig. 6 Dependence of the zirconia ceramics surface area covered with a double chromium-silver
film on the annealing time at different temperatures (900–1100 ºS)
Fig. 7 The joint of zirconia ceramics, through a double film of Cr–Ag, with ultrathin welding seam
which was made by pressure welding, ×600