7 Impact Resistance of Armor Steel/Ceramic/UHPCC Layered …
broken and the residual mass and length were not obtained. “–” represents that the
armor steel plate was not perforated and the damage of UHPCC was ignored. In
Table 7.13, the test data of striking velocity V 0 and DOP are listed. It should be
noted that DOP contains the thickness of penetrated armor steel plate. Besides, the
residual length and mass of the recovered projectiles denoted respectively by L r and
M r are also listed in Table 7.13. The corresponding damage and failure of recovered
projectiles, armor steel plates and UHPCC targets in each shot are shown in Fig. 7.35.
d1
d2
d3
d4
Fig. 7.35 Damage of projectiles, armor steel plates and UHPCC targets
7 Impact Resistance of Armor Steel/Ceramic/UHPCC Layered …
broken and the residual mass and length were not obtained. “–” represents that the
armor steel plate was not perforated and the damage of UHPCC was ignored. In
Table 7.13, the test data of striking velocity V 0 and DOP are listed. It should be
noted that DOP contains the thickness of penetrated armor steel plate. Besides, the
residual length and mass of the recovered projectiles denoted respectively by L r and
M r are also listed in Table 7.13. The corresponding damage and failure of recovered
projectiles, armor steel plates and UHPCC targets in each shot are shown in Fig. 7.35.
d1
d2
d3
d4
Fig. 7.35 Damage of projectiles, armor steel plates and UHPCC targets